Kinetics of polymerization and particle stabilization mechanism on dispersion copolymerization of styrene and divinylbenzene
Citations Over TimeTop 12% of 2002 papers
Abstract
Abstract Monodisperse highly crosslinked microspheres were prepared by dispersion copolymerization of styrene and divinylbenzene in an ethanol/water medium using poly(N‐vinylpyrrolidone) (PVP) as the stabilizer. The locus of polymerization and growth of particles were investigated. The polymerization kinetics, average particle diameter ( D n ), polydispersity index (PDI), and numbers of particles ( N p ) were presented. When the initial styrene concentration is below 20%, the results indicate that the polymerization occurs in the particles, and the particles grow to their final size by the diffusion of monomer and oligomer into the existing particles. The polymerization rate can be described by the equation R p = k [ l ] 0.87 ([St] 1.91 + [DVB] 0.09 ) (1 + [PVP] 0.01 ) exp(− 45.35/ RT ). The data from infrared spectroscopy demonstrated that the graft stabilizer was present. The dissolution experiments show that the crosslinking reaction occurred irregularly in batch dispersion polymerization. Using the postaddition approach, up to 3% divenylbenzene (DVB) was successfully incorporated in the synthesis of coagulum‐free substance, and monodisperse crosslinked 5 μ m microspheres with a superior resistance to solvents have been prepared. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 85: 2230–2238, 2002
Related Papers
- → Synthesis of monodisperse polystyrene microspheres by dispersion polymerization using sodium polyaspartate(2007)20 cited
- → Monomer Reactivity Ratios from High Conversion Copolymerization of Styrene with meta- and with para-Divinylbenzene(1970)23 cited
- → Coating of poly(styrene-co-divinylbenzene) beads with copolymer of styrene and divinylbenzene(1984)1 cited
- → Effect of electron-donor compounds on the copolymerization of styrene and its derivatives in the presence of SnCl4 and TiCl4(1983)
- → Redox ion exchangers based on sulfochlorinated copolymers of styrene and divinylbenzene(1970)