Degradation of low density polyethylene during extrusion. I. Volatile compounds in smoke from extruded films

Citations Over TimeTop 15% of 2002 papers

Abstract

Abstract Many problems with odor and taste in food packaging can be traced to degradation of the packaging materials during processing. From this starting point, the degradation of polyethylene in a commercial extrusion coating process was studied by analyzing degradation products present in smoke sampled at the extruder die orifice. Two low‐density polyethylenes, A and B, with similar melt flow indexes and densities and obtained from different producers, were investigated. A third polymer, C, consisting of recycled material B, was also investigated. More than 40 aliphatic aldehydes and ketones, together with 14 different carboxylic acids, were identified in the smoke. The highest concentration was found for acetaldehyde, regardless of polymer and processing conditions. Increasing the extrusion temperatures in the range 280–325 °C increased the amounts of the oxidized products in the smoke. The extruded film thickness, 12 and 25 μm, influenced the concentrations of degradation products, with the thicker film giving higher amounts of product. The recycled polymer C generally gave lower concentrations of degradation products compared with the virgin polymer B. Differences in the product spectrum between the two virgin polymers may be related to differences in the manufacturing process. Many of the identified compounds have very characteristic taste and smell and are consequently of interest from an odor and taste point of view in food packaging applications. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 1580–1586, 2002

Related Papers

• → Space charge behavior in low-density polyethylene(2000)86 cited
• → Effect of suppression layer on space charge formation in low-density polyethylene(2002)2 cited
• → Study of biodegradability of LDPE, PS, PVC and UF concealed in soil for over 32years.(1993)5 cited
• → Space charge behaviors in low-density polyethylene(2003)4 cited
• → Μελέτη της επίδρασης ιονιζουσών ακτινοβολιών-γ και ηλεκτρονίων υψηλής ενέργειας στις φυσικοχημικές και μηχανικές ιδιότητες πολυστρωματικών υλικών συσκευασίας τροφίμων(2007)