Pyrolysis of epoxy resins and fire behavior of epoxy resin composites flame‐retarded with 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide additives

Citations Over TimeTop 10% of 2007 papers

Abstract

Abstract The pyrolysis of an epoxy resin and the fire behavior of corresponding carbon fiber‐reinforced composites, both flame‐retarded with either 10‐ethyl‐9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene 10‐oxide or 1,3,5‐tris[2‐(9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene 10‐oxide‐10‐)ethyl]1, 3,5‐triazine‐2,4,6(1H,3H,5H)‐trione, are investigated. The different fire retardancy mechanisms are discussed, and their influence on the fire properties assessed, in particular for flammability (limiting oxygen index, UL 94) and developing fires (cone calorimeter with different external heat fluxes of 35, 50, and 70 kW m −2 ). Adding the flame retardants containing 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide affects the fire behavior by both condensed phase and gas phase mechanisms. Interactions between the additives and the epoxy resin result in a change in the decomposition pathways and an increased char formation. The release of phosphorous products results in significant flame inhibition. The fire properties achieved are thus interesting with respect to industrial exploration. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 2260–2269, 2007

Related Papers

• → Flammability parameters of wood tested on a cone calorimeter(2001)146 cited
• → Preparation and flame retardant properties of EVA/Mg(OH)₂/La₂O₃composites(2010)8 cited
• Evaluation of fire-retardant wood treated with poly-phosphatic carbamate using a cone calorimeter(2003)
• → Synthesis and Characterization of Phosphorus-Containing Flame Retardant Polyamide 66(2020)1 cited
• Formula of Flame Retardant HIPS by Uniform Design(2009)