Carboxyl‐terminated butadiene acrylonitrile rubber/epoxy polymer alloys as damping adhesives and energy absorbable resins

Citations Over TimeTop 13% of 2007 papers

Abstract

Abstract Carboxyl‐terminated butadiene acrylonitrile (CTBN) liquid rubber/epoxy (diglycidyl ether of bisphenol‐A: DGEBA) / diamino diphenyl methane (DDM) resins, in which CTBN was 60 wt % as the major component, were formulated to evaluate the damping and adhesive properties. In cases where acrylonitrile (AN) was 10∼18 mol % as copolymerization ratio in CTBN, the blend resins showed micro‐phase separated morphologies with rubber‐rich continuous phases and epoxy‐rich dispersed phases. The composite loss factors (η) for steel laminates, which consisted of two steel plates with a resin layer in between, depended highly on the environmental temperature and the resonant frequencies. On the other hand, in the case where AN was 26 mol % in CTBN, the cured resin did not show clear micro‐phase separation, which means the components achieve good compatibility in nano‐scale. This polymer alloy had a broad glass‐transition temperature range, which resulted in the high loss factor (η > 0.1) for the steel laminates and excellent energy absorbability as the bulk resin in a broad temperature range. Also the resin indicated high adhesive strengths to aluminum substrates under both shear and peel stress modes. The high adhesive strengths of the CTBN/epoxy polymer alloy originated in the high strength and the high strain energy to failure of the bulk resin. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007

Related Papers

• → Vulcanization Kinetic Study of Different Nitrile Rubber (NBR) Compounds(2014)5 cited
• → Thermal degradation of a diglycidyl ether of bisphenol A/1,3-bisaminomethylcyclohexane (DGEBA/1,3-BAC) epoxy resin system(1995)19 cited
• → NR/NBR blends — basic problems and solutions(1998)9 cited
• → Preparation of a cured epoxy resin by the room temperature reaction of bisphenol a diglycidyl ether with polyamines(1998)
• Effect of Hydroxyl Mobility on the Cure Kinetics of Diglycidyl Ether of Bisphenol A (DGEBA) Epoxy in the Presence of a Tertiary Amine(2018)