Electrospinning of poly(vinyl pyrrolidone): Effects of solvents on electrospinnability for the fabrication of poly(p‐phenylene vinylene) and TiO₂ nanofibers

Citations Over TimeTop 11% of 2009 papers

Abstract

Abstract Seven different solvents (methanol, ethanol, 2‐propanol, 1,2‐dichloroethane, water, chloroform, and dichloromethane) were used to prepare electrospun poly(vinyl pyrrolidone) (PVP) fibers. The dielectric constant, viscosity, and surface tension of the solvents essentially affected the electrospinnability, morphological appearance, and size of the as‐spun fibers. Small and uniform as‐spun fibers could be fabricated from PVP solutions in solvents with a significantly high dielectric constant, low surface tension, and low viscosity. In three alcohol solutions (e.g., methanol, ethanol, and 2‐propanol), the diameters of as‐spun PVP fibers decreased with the dielectric constant, dipole moment, and density of the solvents increasing and with the viscosity of the solvents decreasing. Among these solvents, methanol was the best solvent, providing fibers with an optimal morphological appearance and a small fiber diameter. Mixing an unspinnable solvent with a solvent with a high dielectric constant, low surface tension, and low viscosity could increase the electrospinnability of the solution. The effects of solution properties and spinning conditions on the morphological appearance and diameter of electrospun PVP fibers were also carefully investigated. Under all investigated conditions for the electrospinning of a PVP solution in ethanol, the average diameters of the as‐spun fibers ranged from 200 nm to 1.5 μm. Well‐aligned PVP fibers were also produced with a rotating‐drum collector technique. Lastly, PVP was used in the fabrication of poly[2‐methoxy‐5‐(2′‐ethylhexyloxy)‐1,4‐phenylene‐vinylene] and TiO 2 fibers by acting as a polymer carrier or guide. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009

Related Papers

• → Structural Control of Nanofibers According to Electrospinning Process Conditions and Their Applications(2023)33 cited
• → Nanofibers: principles and manufacture(2012)26 cited
• → Controlling the architecture of nanofiber‐coated microfibers using electrospinning(2010)9 cited
• Recent developments in electrospinning of nanofibers and nanofiber yarns(2010)
• Preparation and application of PANI / PEO nanofiber sensor based on electrospinning(2015)