Pebax‐1657 nanocomposite membranes incorporated with nanoparticles/colloids/carbon nanotubes for CO2/N2 and CO2/H2 separation
Citations Over TimeTop 1% of 2013 papers
Abstract
ABSTRACT Pebax‐1657 is known as a promising polymeric membrane material for CO 2 /N 2 and CO 2 /H 2 separation. In order to further improve its gas separation performance and reinforce the membrane, different fillers including silica nanoparticles, polystyrene (PS) colloids, and carbon nanotubes (CNTs) were incorporated into the polymer matrix to form nanocomposite membranes. The nanocomposite membranes of Pebax‐1657/silica and Pebax‐1657/PS colloid had a decreased CO 2 permeability and selectivity over N 2 or H 2 compared to the pure Pebax‐1657 membrane, while the Pebax‐1657/CNT nanocomposite membranes had an increased CO 2 permeability, retaining similar CO 2 /N 2 or CO 2 /H 2 selectivity compared to the pure polymer membrane. The CO 2 permeability increased with increasing CNT content and reached a maximum at 5 wt % CNTs. The CNT‐enhanced gas permeability was attributed to the increase in gas diffusivity. The tensile modulus of Pebax‐1657 increased 43% after adding 5 wt % single‐wall CNTs (SWNTs), and increased 24% after adding 5 wt % multi‐wall CNTs (MWNTs). Thus, it is feasible to add CNTs to Pebax‐1657 membranes for improved mechanical strength and gas separation performance. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 130: 2867–2876, 2013
Related Papers
- → Catalytic degradation of polystyrene into styrene and a design of recyclable polystyrene with dispersed catalysts(2000)172 cited
- → Analysis of permeation transients of pure gases through dense polymeric membranes measured by a new permeation apparatus(2000)50 cited
- → Gas-driven hydrogen permeation in the surface-limited regime(2003)16 cited
- → Photo-oxidation of polystyrene film: 2. Photo-oxidation of polystyrene film with light absorbed by the polystyrene-oxygen complex(1978)14 cited
- → General Formula of Tritium Permeation through Plasma Facing Materials.(1999)