The influence of montmorillonite on the flame‐retarding properties of intumescent bio‐based PLA composites

Citations Over Time

Abstract

Abstract Biobased flame‐retardant polylactic acid composites were prepared using ammonium polyphosphate (AP), lignin, and a raw montmorillonite (ANa) as the intumescent formulation. The concentration of AP and of ANa was varied in order to study its influence on the flammability properties of the composites. The samples were submitted to cone calorimeter test, thermogravimetric analysis coupled to Fourier‐transform infrared spectroscopy (TGA‐FTIR), limiting oxygen index (LOI), and UL‐94 vertical burn. The cone calorimeter residues were analysed through scanning electronic microscopy, X‐ray diffraction, and FTIR. The results show that the combined addition of the intumescent formulation and the ANa leads to an improvement in the fire behavior of the composites, compared with that of the neat polymer. The best fire‐retardant performance was achieved by using the highest AP concentration (17%) and the lowest ANa concentration (1.2%), reaching a LOI value of 39%.

Related Papers

• → Study of the mechanism of intumescence in fire retardant polymers: Part II—Mechanism of action in polypropylene-ammonium polyphosphate-pentaerythritol mixtures(1984)180 cited
• → XPS study of an intumescent coating application to the ammonium polyphosphate/pentaerythritol fire-retardant system(1994)152 cited
• → Study of the mechanism of intumescence in fire retardant polymers: Part III—Effect of urea on the ammonium polyphosphate-pentaerythritol system(1984)80 cited
• → Intumescent polypropylene/flax blends: a preliminary study(2004)79 cited
• → Thermoanalytical studies of intumescent systems(1993)16 cited