Carbon Dioxide Adsorption in Amine‐Functionalized Mixed‐Ligand Metal–Organic Frameworks of UiO‐66 Topology

Citations Over TimeTop 10% of 2014 papers

Abstract

A series of mixed-ligand [1,4-benzenedicarboxylic acid (BDC)/2-amino-1,4-benzenedicarboxylic acid (ABDC)] UiO-66 metal-organic frameworks (MOFs) synthesized through two different methods (low (LT) and high temperature (HT)) have been investigated for their carbon dioxide adsorption properties from 0 to 1 bar to clarify the role of amino loading on carbon dioxide uptake. Volumetric CO2 isotherms show that the CO2 capacity (normalized to the Langmuir surface area) increases with a degree of functionalization of about 46%; for similar NH2 contents, the same values are found for both synthetic procedures. Microcalorimetric isotherms reveal that amino-functionalized materials have a larger differential heat of adsorption (q(diff) ) towards CO2 ; reaching 27(25) and 20(22) kJ mol(-1) on HT(LT)-UiO-66-NH2 and UiO-66, respectively, at the lowest equilibrium pressures used in this study. All experimental results are supported by values obtained through quantum mechanical calculations.

Related Papers

• → Maskless functionalization of a carbon nanotube dot array biosensor using an ultrafine atmospheric pressure plasma jet(2015)47 cited
• → Surface functionalization of microporous carbon fibers by vapor phase methods for CO2 capture(2023)3 cited
• → Selective external surface functionalization of large-pore silica materials capable of protein loading(2016)24 cited
• → Thermal Functionalization of GaN Surfaces with 1-Alkenes(2013)13 cited
• → Nitrilotriacetic acid functionalization on Fe3O4 nanoparticle via amino and carboxylic functionalization(2020)2 cited