Effect of Halide Composition on the Photochemical Stability of Perovskite Photovoltaic Materials
Citations Over TimeTop 10% of 2016 papers
Abstract
The photochemical stability of encapsulated films of mixed halide perovskites with a range of MAPb(I1-x Brx )3 (MA=methylammonium) compositions (solid solutions) was investigated under accelerated stressing using concentrated sunlight. The relevance of accelerated testing to standard operational conditions of solar cells was confirmed by comparison to degradation experiments under outdoor sunlight exposure. We found that MAPbBr3 films exhibited no degradation, while MAPbI3 and mixed halide MAPb(I1-x Brx )3 films decomposed yielding crystallization of inorganic PbI2 accompanied by degradation of the perovskite solar light absorption, with faster absorption degradation in mixed halide films. The crystal coherence length was found to correlate with the stability of the films. We postulate that the introduction of Br into the mixed halide solid solution stressed its structure and induced more structural defects and/or grain boundaries compared to pure halide perovskites, which might be responsible for the accelerated degradation. Hence, the cause for accelerated degradation may be the increased defect density rather than the chemical composition of the perovskite materials.
Related Papers
- → Organolead Halide Perovskite: New Horizons in Solar Cell Research(2014)709 cited
- → Machine learning for halide perovskite materials(2020)118 cited
- → Unraveling the Role of Monovalent Halides in Mixed‐Halide Organic–Inorganic Perovskites(2015)13 cited
- → Aggregation of molecular halide perovskite Cs4PbX6: A first-principles investigation(2019)7 cited
- → Modifying Optoelectronic Properties of Molecular Halide Perovskite Cs4PbBr6 via Organic Ligands: A First-Principles Investigation(2021)