Flame‐Retarded Epoxy Resins with a Curing Agent of DOPO‐Triazine Based Anhydride
Citations Over TimeTop 10% of 2016 papers
Abstract
A 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide (DOPO)‐triazine based anhydride (2,4,6‐tris‐(DOPO‐methylformatephthalic anhydride‐phenoxy)‐1,3,5‐triazine (TDA)) is synthesized and used as a halogen‐free flame retardant co‐curing agent for diglycidyl ether of bisphenol A/methylhexahydrophthalic anhydride (DGEBA/MHHPA) system. The conjugation of anhydride group is increased by the utilization of TDA, leading to the reduction in the curing activation energy. The cured epoxy resin passes V‐0 rating of UL 94 test with the limiting oxygen index of 32.7 vol% when the phosphorus content is only 1.5 wt%. The flame‐retarding action of triazine ring and DOPO moiety is investigated by the residue analysis and the characterization of pyrolysis gas. Due to the presence of bulky aromatic subunits in the molecular structure of TDA, the flame‐retarded epoxy resins maintain the high glass transition temperature of DGEBA/MHHPA. Besides, the moisture absorption is diminished following the usage of TDA. image
Related Papers
- → Synthesis and properties of epoxy resins containing bis(3-hydroxyphenyl) phenyl phosphate(2000)78 cited
- → Flame retardant epoxy resins based on diglycidyl ether of (2,5‐dihydroxyphenyl)diphenyl phosphine oxide(2007)57 cited
- → Synthesis and characterization of P/Si flame retardant and its application in epoxy systems(2011)15 cited
- Flame Retardancy Study on Phosphorus-Containing Epoxy Resin Synthesized by the Reaction of DOPO and the Diglycidyl Ether of Bisphenol A(2006)
- → Preparation and characterization of high molecular weight poly(hydroxy ethers) with unusually high glass transition temperatures(1992)10 cited