Synthesis and properties of room temperature curable trimethoxysilane‐terminated polyurethane and their dispersions

Citations Over TimeTop 24% of 2007 papers

Abstract

Abstract The purpose of this research is to study the synthesis and characterization of stable aqueous dispersions of externally chain extended polyurethane/urea compositions terminated by hydrolyzable or hydrolyzed trialkoxysilane groups incorporated through secondary amino groups. These dispersions with excellent storage stability are substantially free from organic solvents which cure to water and solvent resistant, tough, scratch resistant, preferably light stable (non‐yellowing) silylated polyurethane (SPU) films. The films were characterized by FT‐IR, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), tensile strength and water contact angle measurements, nanoindentation, gel content, water and xylene swellability tests. The properties of the films were discussed and correlated in detail by changing length of soft segment, diisocyanates, NCO/OH ratio and chain extender, ethylenediamine (EDA). From the results, it was found that the particle size and viscosity are lower whereas the gel content and thermal stability are higher for SPUs. Modulus, hardness and tensile properties of SPU films are superior compared to EDA‐PU film. Higher water contact angle and residual weight percentage of SPU films confirm silylation of PU by [3‐(phenylamino)propyl]trimethoxysilane (PAPTMS). Increase in NCO/OH ratios consumes more quantity of PAPTMS which makes PU with superior mechanical properties. Higher PAPTMS content in SPU results in effective crosslinking of the functional silanol groups formed by hydrolysis reaction of trimethoxysilane groups. Overall, SPUs synthesized at 1.4 NCO/OH ratio using Poly‐(oxytetramethylene)glycol (PTMG)‐2000 and isophorone diisocyanate (or) toluene‐2,4‐diisocyanate have excellent properties compared to SPUs prepared using PTMG‐1000 and at 1.2 and 1.6 NCO/OH ratios. SPUs prepared at 1.6 NCO/OH ratio are brittle due to higher crosslinking density. In addition, the crosslinking density of the films can be modified through silane end‐group modification to produce SPUs with a wide range of physical properties. Copyright © 2007 John Wiley & Sons, Ltd.

Related Papers

• → Preparation and characterization of waterborne polyurethane based on diphenylmethane diisocyanate‐50(2016)23 cited
• → Preparation and Characterization of Waterborne Polyurethane Crosslinked by Urea Bridges(2011)18 cited
• Study on synthesis and application of blocked waterborne polyurethane(2010)
• Preparation and Study on Properties of Castor Oil based Waterproof UV- curable Waterborne Polyurethane Coatings(2015)
• Synthesis and application of modified aqueous polyurethane woolshrink-resisting agents(2004)