Preparation and Performance of a HNIW/TNT Cocrystal Explosive

Citations Over TimeTop 10% of 2013 papers

Abstract

Abstract A novel cocrystal explosive composed of 2,4,6,8,10,12‐hexanitrohexaazaiso‐wurtzitane (HNIW) and 2,4,6‐trinitrotoluene (TNT) in a 1 : 1 molar ratio was effectively prepared by solvent/nonsolvent cocrystallization adopting dextrin as modified additive. The structure, thermal behavior, sensitivity, and detonation properties of HNIW/TNT cocrystal were studied. The morphology and structure of the cocrystal were characterized by scanning electron microscopy (SEM) and single crystal X‐ray diffraction (SXRD). SEM images showed that the cocrystal has a prism type morphology with an average size of 270 μm. SXRD revealed that the cocrystal crystallizes in the orthorhombic system, space group Pbca , and is formed by hydrogen bonding interactions. The properties of the cocrystal including sensitivity, thermal decomposition, and detonation performances were discussed in detail. Sensitivity studies showed that the cocrystal exhibits low impact and friction sensitivity, and largely reduces the mechanical sensitivity of HNIW. DSC and TG tests indicated that the heterogeneous exothermic decomposition of the cocrystal occurs in the temperature range from 170 °C to 265 °C with peak maxima at 220 °C and 250 °C and significantly increases the melting point of TNT by 54 °C. The cocrystal has excellent detonation properties with a detonation velocity of 8426 m s −1 and a calculated detonation pressure of 32.3 MPa at a charge density of 1.76 g cm −3 , respectively. Moreover, the results suggested that the HNIW/TNT cocrystal not only has unique performance itself, but also effectively alters the properties of TNT and HNIW. Therefore, the cocrystal formed by HNIW and TNT could provide a new and effective method to modify the properties of certain compounds to yield enhanced explosives for further application.

Related Papers

• → The Kamlet‐Jacobs Parameter φ: A Measure of Intrinsic Detonation Potential(2019)19 cited
• → Preparation of LLM‐105‐Based Explosive Ink and Its Detonating Transfer Performance in Explosive Network(2022)4 cited
• Experimental Research of the Charge Defects' Influence on Detonation Velocity of Melting-Cast Explosive(2011)
• → Unified form EOS for detonation products based on relationship between initial density and detonation velocity(2020)1 cited
• → Divergent Detonation Wave Processes in PBX Based on RDX(2004)