Novel naturally crosslinked electrospun nanofibrous chitosan mats for guided bone regeneration membranes: material characterization and cytocompatibility

Citations Over TimeTop 20% of 2012 papers

Abstract

Guided bone regeneration (GBR) barrier membranes are used to prevent soft tissue infiltration into the graft space during dental procedures that involve bone grafting. Chitosan materials have shown promise as GBR barrier membranes, due to their biocompatibility and predictable biodegradability, but degradation rates may still be too high for clinical applications. In this study, chitosan GBR membranes were electrospun using chitosan (70% deacetylated, 312 kDa, 5.5 w/v%), with or without the addition of 5 or 10 mm genipin, a natural crosslinking agent, in order to extend the degradation to meet the clinical target time frame of 4-6 months. Membranes were evaluated for fibre diameter, tensile strength, biodegradation rate, bond structure and cytocompatibility. Genipin addition, at 5 or 10 mm, resulted in median fibre diameters 184, 144 and 154 nm for uncrosslinked, 5 mm and 10 mm crosslinked, respectively. Crosslinking, examined by Fourier transform infrared spectroscopy, showed a decrease in N-H stretch as genipin levels were increased. Genipin-crosslinked mats exhibited only 22% degradation based on mass loss, as compared to 34% for uncrosslinked mats at 16 weeks in vitro. The ultimate tensile strength of the mats was increased by 165% to 32 MPa with 10 mm crosslinking as compared to the uncrosslinked mats. Finally, genipin-crosslinked mats supported the proliferation of SAOS-2 cells in a 5 day growth study, similar to uncrosslinked mats. These results suggest that electrospun chitosan mats may benefit from genipin crosslinking and have the potential to meet clinical degradation time frames for GBR applications.

Related Papers

• → Stabilization of gelatin films by crosslinking with genipin(2002)622 cited
• → Genipin, a natural blue colorant precursor: Source, extraction, properties, and applications(2023)98 cited
• → Study of Genipin Behavior in Neutral and Acidic Aqueous Solutions at Elevated Temperatures(2023)9 cited
• → A Polymeric Delivery System Enables Controlled Release of Genipin for Spatially-Confined In Situ Crosslinking of Injured Connective Tissues(2020)2 cited
• Crosslinking Reaction of Chitosan and Gelatin with Genipin(2007)