Nanosecond and Femtosecond Laser Ablation of Brass: Particulate and ICPMS Measurements
Citations Over TimeTop 10% of 2003 papers
Abstract
Femtosecond and nanosecond lasers were compared for ablating brass alloys. All operating parameters from both lasers were equal except for the pulse duration. The ablated aerosol vapor was collected on silicon substrates for particle size measurements or sent into an inductively coupled plasma mass spectrometer. The diameters and size distribution of particulates were measured from scanning electron microscope (SEM) images of the collected ablated aerosol. SEM measurements showed that particles ablated using nanosecond pulses were single spherical entities ranging in diameter from several micrometers to several hundred nanometers. Primary particles ablated using femtosecond ablation were approximately 100 nm in diameter but formed large agglomerates. ICPMS showed enhanced signal intensity and stability using femtosecond compared to nanosecond laser ablation.
Related Papers
- → Enhanced optical emission in laser-induced breakdown spectroscopy by combining femtosecond and nanosecond laser pulses(2020)29 cited
- → Comparison of emission signals for femtosecond and nanosecond laser-ablated Cu plasmas by changing the distance from focusing-lens to target-surface at different target temperatures(2021)8 cited
- → Supercontinuum generation beyond 2 µm in GeO2fiber: comparison of nano- and femtosecond pumping(2015)13 cited
- → The comparison of fabricating colorful patterns on stainless steel with femtosecond and nanosecond laser pulses(2011)1 cited
- → Nanosecond interrogation of surface plasmon resonance sensors using chirped femtosecond optical pulses(2008)