Hybrid Bionanocomposite Containing Magnesium Hydroxide Nanoparticles Embedded in a Carboxymethyl Cellulose Hydrogel Plus Silk Fibroin as a Scaffold for Wound Dressing Applications

Citations Over TimeTop 10% of 2021 papers

Abstract

Based on the promising biomedical developments in wound healing strategies, herein, a new nanobiocomposite scaffold was designed and presented by incorporation of carboxymethyl cellulose hydrogels prepared using epichlorohydrin as a cross-linking agent (CMC hydrogel), a natural silk fibroin (SF) protein, and magnesium hydroxide nanoparticles (Mg(OH)₂ NPs). Biological evaluation of the CMC hydrogel/SF/Mg(OH)₂ nanobiocomposite scaffold was conducted via in vitro cell viability assays and in vivo assays, red blood cell hemolysis, and antibiofilm assays. Considering the cell viability percentage of Hu02 cells (84.5%) in the presence of the prepared nanobiocomposite after 7 days, it was indicated that this new nanoscaffold was biocompatible. The signs of excellent hemocompatibility and the high antibacterial activity were observed due to the low-point hemolytic effect (8.3%) and high-level potential in constraining the P. aeruginosa biofilm formation with a low OD value (0.13). Moreover, in vivo wound healing assay results indicated that the wound healing method was faster in mice treated with the prepared nanobiocomposite scaffold (82.29%) than the control group (75.63%) in 12 days. Apart from the structural characterization of the CMC hydrogel/SF/Mg(OH)₂ nanobiocomposite through FTIR, EDX, FESEM, and TG analyses, compressive mechanical tests, contact angle, porosity, and swelling ratio studies indicated that the combination of the CMC hydrogel structure with SF protein and Mg(OH)₂ NPs could significantly impact Young's modulus (from 11.34 to 10.14 MPa), tensile strength (from 299.35 to 250.78 MPa), elongation at break (12.52 to 12.84%), hydrophilicity, and water uptake capacity (92.5%).

Related Papers

• → Raman spectroscopic characterization of Bombyx mori silk fibroin: Raman spectrum of Silk I(2001)156 cited
• → Tuning the structure and performance of silk biomaterials by combining mulberry and non-mulberry silk fibroin(2017)37 cited
• → Design, Expression and Solid-State NMR Characterization of Silk-Like Materials Constructed from Sequences of Spider Silk, Samia cynthia ricini and Bombyx mori Silk Fibroins(2005)31 cited
• → Phosphorylation of silk fibroins improves the cytocompatibility of silk fibroin derived materials: A platform for the production of tuneable material(2014)9 cited
• Biological and physical aspects(2000)