Vanadium-Tailored Silicon Composite with Furthered Ion Diffusion Behaviors for Longevity Lithium-Ion Storage

Citations Over TimeTop 10% of 2023 papers

Abstract

As one of the promising anode materials, silicon has attracted much attention due to its high theoretical specific capacity (∼3579 mAh g-1) and suitable lithium alloying voltage (0.1-0.4 V). Nevertheless, the enormous volume expansion (∼300%) in the process of lithium alloying has a great negative effect on its cyclic stability, which seriously restricts the large-scale industrial preparation of silicon anodes. Herein, we design a facile synthesis strategy combining vanadium doping and carbon coating to prepare a silicon-based composite (V-Si@C). The prepared V-Si@C composite does not merely show improved conductivity but also improved electrochemical kinetics, attributed to the enlarged lattice spacing by V doping. Additionally, the superiority of this doping strategy accompanied by microstructure change is embodied in the relieved volume changes during the repeated charging/discharging process. Notably, the initial capacity of the advanced V-Si@C electrode is 904 mAh g-1 (1 A g-1) and still holds at 1216 mAh g-1 even after 600 cycles, showing superior electrochemical performance. This study offers an alternative direction for the large-scale preparation of high-performance silicon-based anodes.

Related Papers

• → Reduction of vanadium(V) to vanadium(IV) by NADPH, and vanadium(IV) to vanadium(III) by cysteine methyl ester in the presence of biologically relevant ligands(2007)23 cited
• → Vanadium and Vanadium Compounds(2000)50 cited
• → Effect of Ligands on the Iron(III)/Iron(II) System and Its Novel Application to the Simultaneous Flow Injection Determination of Vanadium(IV) and Vanadium(V)(1994)14 cited
• Vanadium Recovery from Vanadium-containing Leaching Solution with High Iron Concentration by Reducing Precipitating-Redissolving(2012)