Covalent Functionalization of Silicon with Plasma-Grown “Fuzzy” Graphene: Robust Aqueous Photoelectrodes for CO₂ Reduction by Molecular Catalysts

Citations Over Time

Abstract

Carbon electrodes are ideal for electrochemistry with molecular catalysts, exhibiting facile charge transfer and good stability. Yet for solar-driven catalysis with semiconductor light absorbers, stable semiconductor/carbon interfaces can be difficult to achieve, and carbon's high optical extinction means it can only be used in ultrathin layers. Here, we demonstrate a plasma-enhanced chemical vapor deposition process that achieves well-controlled deposition of out-of-plane "fuzzy" graphene (FG) on thermally oxidized Si substrates. The resulting Si|FG interfaces possess a silicon oxycarbide (SiOC) interfacial layer, implying covalent bonding between Si and the FG film that is consistent with the mechanical robustness observed from the films. The FG layer is uniform and tunable in thickness and optical transparency by deposition time. Using p-type Si|FG substrates, noncovalent immobilization of cobalt phthalocyanine (CoPc) molecular catalysts was employed for the photoelectrochemical reduction of CO₂ in aqueous solution. The Si|FG|CoPc photocathodes exhibited good catalytic activity, yielding a current density of ∼1 mA/cm2, Faradaic efficiency for CO of ∼70% (balance H₂), and stable photocurrent for at least 30 h at -1.5 V vs Ag/AgCl under 1-sun illumination. The results suggest that plasma-deposited FG is a robust carbon electrode for molecular catalysts and suitable for further development of aqueous-stable Si photocathodes for CO₂ reduction.

Related Papers

• → The effect of substrates on the Raman spectrum of graphene: Graphene- on-sapphire and graphene-on-glass(2007)250 cited
• A natural advantage? Using mined graphite to make graphene(2013)
• Synthesis and Characterisation of Graphene Single Sheets(2012)
• Unique synthesis of graphene-based materials for clean energy and biological sensing applications(2012)
• → Orthotropic friction at the edges and interior of graphene and graphene fluoride and frictional anisotropy of graphene at the nanoscale(2021)