Ultrathin ZnS and ZnO Interfacial Passivation Layers for Atomic-Layer-Deposited HfO2 Films on InP Substrates
Citations Over TimeTop 20% of 2016 papers
Abstract
Ultrathin ZnS and ZnO films grown by atomic layer deposition (ALD) were employed as interfacial passivation layers (IPLs) for HfO2 films on InP substrates. The interfacial layer growth during the ALD of the HfO2 film was effectively suppressed by the IPLs, resulting in the decrease of electrical thickness, hysteresis, and interface state density. Compared with the ZnO IPL, the ZnS IPL was more effective in reducing the interface state density near the valence band edge. The leakage current density through the film was considerably lowered by the IPLs because the film crystallization was suppressed. Especially for the film with the ZnS IPL, the leakage current density in the low-voltage region was significantly lower than that observed for the film with the ZnO IPL, because the direct tunneling current was suppressed by the higher conduction band offset of ZnS with the InP substrate.
Related Papers
- → Passivation and Surface Film Formation(1996)7 cited
- → Elimination of parasitic effects in floating junction rear surface passivation for solar cells(1996)17 cited
- → Sulfur passivation of 3C-SiC thin film(2018)4 cited
- Development of High Performance Chromium-Free Passivation Agent Suitable for Coating of Aluminum Alloy and Optimization of Passivation Technology(2012)
- Passivation method of 317L stainless steel used in medicine(2002)