Oxygen-Content-Controllable Graphene Oxide from Electron-Beam-Irradiated Graphite: Synthesis, Characterization, and Removal of Aqueous Lead [Pb(II)]

Citations Over TimeTop 10% of 2016 papers

Abstract

A high-energy electron beam was applied to irradiate graphite for the preparation of graphene oxide (GO) with a controllable oxygen content. The obtained GO sheets were analyzed with various characterization tools. The results revealed that the oxygen-containing groups of GO increased with increasing irradiation dosages. Hence, oxygen-content-controllable synthesis of GO can be realized by changing the irradiation dosages. The GO sheets with different irradiation dosages were then used to adsorb aqueous Pb(II). The effects of contact time, pH, initial lead ion concentration, and ionic strength on Pb(II) sorption onto different GO sheets were examined. The sorption process was found to be very fast (completed within 20 min) at pH 5.0. Except ionic strength, which showed no/little effect on lead sorption, the other factors affected the sorption of aqueous Pb(II) onto GO. The maximum Pb(II) sorption capacities of GO increased with irradiation dosages, confirming that electron-beam irradiation was an effective way to increase the oxygen content of GO. These results suggested that irradiated GO with a controllable oxygen content is a promising nanomaterial for environmental cleanup, particularly for the treatment of cationic metal ions, such as Pb(II).

Related Papers

• → Sorption of uranyl ions on TiO2: Effects of contact time, ionic strength, concentration and humic substance(2004)43 cited
• → Sorption of Nb(V) on pyrolusite (β-MnO2): Effect of pH, humic acid, ionic strength, equilibration time and temperature(2019)8 cited
• Effect of Ionic Strength,Temperature and Humic Substances Concentration on the Sorption of ~(63)Ni(II) to γ-Al_2O_3(2012)
• Effect of Ionic Strength,pH and Humic Acid on Sorption of Ni(II) on Bentonite(2012)
• Fabrication of Graphene by Cleaving Graphite Chemically(2011)