Coffee-Ring-Free Quantum Dot Thin Film Using Inkjet Printing from a Mixed-Solvent System on Modified ZnO Transport Layer for Light-Emitting Devices
Citations Over TimeTop 10% of 2016 papers
Abstract
Inkjet printing has been considered an available way to achieve large size full-color RGB quantum dots LED display, and the key point is to obtain printed film with uniform and flat surface profile. In this work, mixed solvent of 20 vol % 1,2-dichlorobenzene (oDCB) with cyclohexylbenzene (CHB) was used to dissolve green quantum dots (QDs) with CdSe@ZnS/ZnS core/shell structure. Then, by inkjet printing, a flat dotlike QDs film without the coffee ring was successfully obtained on polyetherimide (PEI)-modified ZnO layer, and the printed dots array exhibited great stability and repeatability. Here, adding oDCB into CHB solutions was used to reduce surface tension, and employing ZnO nanoparticle layer with PEI-modified was used to increase the surface free energy. As a result, a small contact angle is formed, which leads to the enhancement of evaporation rate, and then the coffee ring effect was suppressed. The printed dots with flat surface profile were eventually realized. Moreover, inverted green QD-LEDs with PEI-modified ZnO film as electron transport layer (ETL) and printed green QDs film as emission layer were successfully fabricated. The QD-LEDs exhibited the maximum luminance of 12 000 cd/m2 and the peak current efficiency of 4.5 cd/A at luminance of 1500 cd/m2.
Related Papers
- → Printed Electronics as Prepared by Inkjet Printing(2020)206 cited
- → Controlling Coffee Ring Formation during Drying of Inkjet Printed 2D Inks(2017)118 cited
- → Control and Application of “Coffee Ring” Effect in Inkjet Printing(2015)23 cited
- → Improved performance of inkjet-printed Ag source/drain electrodes for organic thin-film transistors by overcoming the coffee ring effects(2017)9 cited
- → Inkjet-printed Electronics Technology(2022)