Synthesis of Double-Shell SnO₂@C Hollow Nanospheres as Sulfur/Sulfide Cages for Lithium–Sulfur Batteries

Citations Over TimeTop 10% of 2016 papers

Abstract

Double-shell SnO₂@C hollow nanospheres were synthesized by a template method, and then the sulfur was loaded to form a cathode material of S/SnO₂@C composite. In Li-S batteries, it delivered a high initial specific capacity of 1473.1 mAh/g at a current density of 200 mA/g, and the capacity retention was even up to 95.7% over 100 cycles at 3200 mA/g, i.e., a capacity fade rate of only 0.043% per cycle. These good electrochemical performances should be attributed to the SnO₂@C hollow nanospheres. They can enhance the electronic conductivity by the outside carbon shell, and confine the lithium polysulfides by S-Sn-O and S-C chemical bonds to suppress the shuttle effect. Besides, the hollow nanospheres can readily accommodate the sulfur/sulfides to prevent the electrical/mechanical failure of the cathode, instead of their agglomeration on the external surface of SnO₂@C.

Related Papers

• → Self-accelerating sulfur reduction via polysulfide to realize a high-rate sulfidogenic reactor for wastewater treatment(2017)92 cited
• → Graphdiyne-Modified Polyimide Separator: A Polysulfide-Immobilizing Net Hinders the Shuttling of Polysulfides in Lithium–Sulfur Battery(2019)45 cited
• → Electrolyte Design for Low Temperature Lithium‐Sulfur Battery: From Different Polysulfide Conversion Mechanisms(2024)2 cited
• → Vapor Growth Carbon Fiber Felt as an Efficient Interlayer for Trapping Polysulfide in Lithium-Sulfur Battery(2018)7 cited
• → Anodic Oxidation of Alkaline Sulfide Solution at a Low Potential(2011)1 cited