Construction of Core–Shell NiMoO4@Ni-Co-S Nanorods as Advanced Electrodes for High-Performance Asymmetric Supercapacitors
Citations Over TimeTop 1% of 2018 papers
Abstract
In this work, hierarchical core-shell NiMoO4@Ni-Co-S nanorods were first successfully grown on nickel foam by a facile two-step method to fabricate a bind-free electrode. The well-aligned electrode wrapped by Ni-Co-S nanosheets displays excellent nanostructural properties and outstanding electrochemical performance, owing to the synergistic effects of both nickel molybdenum oxides and nickel cobalt sulfides. The prepared core-shell nanorods in a three-electrode cell yielded a high specific capacitance of 2.27 F cm-2 (1892 F g-1) at a current density of 5 mA cm-2 and retained 91.7% of the specific capacitance even after 6000 cycles. Their electrochemical performance was further investigated for their use as positive electrode for asymmetric supercapacitors. Notably, the energy density of the asymmetric supercapacitor device reached 2.45 mWh cm-3 at a power density of 0.131 W cm-3, and still retained a remarkable 80.3% of the specific capacitance after 3500 cycles. There is great potential for the electrode composed of the core-shell NiMoO4@Ni-Co-S nanorods for use in an all-solid-state asymmetric supercapacitor device.
Related Papers
- → A Revisit to Supercapacitor Capacitance Measurement Method 1A of IEC 62391-1(2018)19 cited
- → Extrinsic design of high-performance programmable supercapacitor with large specific areal capacitance(2023)15 cited
- → A high performance symmetrical supercapacitor based on NiCo2O4 nanowires on thin film carbon layer(2018)1 cited
- → Graphene based Supercapacitors with Improved Specific Capacitance and Fast Charging Time at High Current Density(2013)32 cited
- → Synthesis of NiCo2S4@NiMoO4 Nanosheets with Excellent Electrochemical Performance for Supercapacitor(2021)1 cited