Huge Instability of Pt/C Catalysts in Alkaline Medium
Citations Over TimeTop 10% of 2015 papers
Abstract
The stability of carbon-supported electrocatalysts has been largely investigated in acidic electrolytes, but the literature is much scarcer regarding similar stability studies in alkaline medium. Herein, the degradation of Vulcan XC-72-supported platinum nanoparticles (noted Pt/C), a state-of-the-art proton exchange membrane fuel cell electrocatalyst, is investigated in alkaline medium by combining electrochemical measurements and identical location transmission electron microscopy; electrochemical surface area (ECSA) losses were bridged to electrocatalyst morphological changes. The results demonstrate that the degradation in 0.1 M NaOH at 25 °C is severe (60% of ECSA loss after only 150 cycles between 0.1 and 1.23 V vs RHE), which is about 3 times worse than in acidic media for this soft accelerated stress test. Severe carbon corrosion has been ruled out according to Raman spectroscopy and X-ray photoelectron spectroscopy measurements, and it seems that the chemistry of the carbon support (in particular, the interface (chemical bounding)) between the Pt nanoparticles and their carbon substrate does play a significant role in the observed degradations.
Related Papers
- → Mo2C based electrocatalyst with nitrogen doped three-dimensional mesoporous carbon as matrix, synthesis and HER activity study(2018)41 cited
- → Nitrogen-modified metal-organic framework-based carbon: An effective non-precious electrocatalyst for oxygen reduction reaction(2020)17 cited
- → A high performance non-noble metal electrocatalyst for the oxygen reduction reaction derived from a metal organic framework(2016)21 cited
- → Aims of Electrocatalysis(2015)1 cited
- Preparation and characterization of La_(0.6) Ca_(0.4) CoO_3 as bifunctional oxygen electrode electrocatalyst(2004)