Engineering Multilevel Collaborative Catalytic Interfaces with Multifunctional Iron Sites Enabling High-Performance Real Seawater Splitting

Citations Over TimeTop 1% of 2023 papers

Abstract

Given the abundant reserves of seawater and the scarcity of freshwater, real seawater electrolysis is a more economically appealing technology for hydrogen production relative to orthodox freshwater electrolysis. However, this technology is greatly precluded by the undesirable chlorine oxidation reaction and severe chloride corrosion at the anode, further restricting the catalytic efficiency of overall seawater splitting. Herein, a feasible strategy by engineering multifunctional collaborative catalytic interfaces is reported to develop porous metal nitride/phosphide heterostructure arrays anchoring on conductive Ni₂P surfaces with affluent iron sites. Collaborative catalytic interfaces among iron phosphide, bimetallic nitride, and porous Ni₂P supports play a positive role in improving water adsorption/dissociation and hydrogen adsorption behaviors of active Fe sites evidenced by theoretical calculations for hydrogen evolution reactions, and enhancing oxygenated species adsorption and nitrate-rich passivating layers resistant to chloride corrosion for oxygen evolution reaction, thus cooperatively propelling high-performance bifunctional seawater splitting. The resultant material Fe₂P/Ni_1.5Co_1.5N/Ni₂P performs excellently as a self-standing bifunctional catalyst for alkaline seawater splitting. It requires extremely low cell voltages of 1.624 and 1.742 V to afford current densities of 100 and 500 mA/cm2 in 1 M KOH seawater electrolytes, respectively, along with superior long-term stability, outperforming nearly all the ever-reported non-noble bifunctional electrocatalysts and benchmark Pt/IrO₂ coupled electrodes for freshwater/seawater electrolysis. This work presents an effective strategy for greatly enhancing the catalytic efficiency of non-noble catalysts toward green hydrogen production from seawater electrolysis.

Related Papers

• → Hierarchical NiCo₂O₄ Hollow Microcuboids as Bifunctional Electrocatalysts for Overall Water‐Splitting(2016)869 cited
• → Hierarchical NiCo₂O₄ Hollow Microcuboids as Bifunctional Electrocatalysts for Overall Water‐Splitting(2016)631 cited
• → Bifunctional Oxygen Reaction Catalysis of Quadruple Manganese Perovskites(2016)188 cited
• → Engineering hybrid CoMoS4/Ni3S2 nanostructures as efficient bifunctional electrocatalyst for overall water splitting(2019)100 cited
• → Three‐Dimensional Transition Metal Phosphide Heteronanorods for Efficient Overall Water Splitting(2020)32 cited