Characterizing the Three-Dimensional Structure of Block Copolymers via Sequential Infiltration Synthesis and Scanning Transmission Electron Tomography

Citations Over TimeTop 10% of 2015 papers

Abstract

Understanding and controlling the three-dimensional structure of block copolymer (BCP) thin films is critical for utilizing these materials for sub-20 nm nanopatterning in semiconductor devices, as well as in membranes and solar cell applications. Combining an atomic layer deposition (ALD)-based technique for enhancing the contrast of BCPs in transmission electron microscopy (TEM) together with scanning TEM (STEM) tomography reveals and characterizes the three-dimensional structures of poly(styrene-block-methyl methacrylate) (PS-b-PMMA) thin films with great clarity. Sequential infiltration synthesis (SIS), a block-selective technique for growing inorganic materials in BCPs films in an ALD tool and an emerging technique for enhancing the etch contrast of BCPs, was harnessed to significantly enhance the high-angle scattering from the polar domains of BCP films in the TEM. The power of combining SIS and STEM tomography for three-dimensional (3D) characterization of BCP films was demonstrated with the following cases: self-assembled cylindrical, lamellar, and spherical PS-b-PMMA thin films. In all cases, STEM tomography has revealed 3D structures that were hidden underneath the surface, including (1) the 3D structure of defects in cylindrical and lamellar phases, (2) the nonperpendicular 3D surface of grain boundaries in the cylindrical phase, and (3) the 3D arrangement of spheres in body-centered-cubic (BCC) and hexagonal-closed-pack (HCP) morphologies in the spherical phase. The 3D data of the spherical morphologies was compared to coarse-grained simulations and assisted in validating the simulations' parameters. STEM tomography of SIS-treated BCP films enables the characterization of the exact structure used for pattern transfer and can lead to a better understating of the physics that is utilized in BCP lithography.

Related Papers

• → Mechanism of the Transition between Lamellar and Gyroid Phases Formed by a Diblock Copolymer in Aqueous Solution(2004)56 cited
• → Kinetic pathway of lamellar → gyroid transition: Pretransition and transient states(2001)38 cited
• → Mesoporous Polystyrenes via Lamellar Block Copolymer Assembly(2013)3 cited
• → Interface between Lamellar and Gyroid Structures in Diblock Copolymer Melts(2007)9 cited
• → Fluctuation Modes Prior to Lamellar-Double Gyroid Transition of a Nonionic Surfactant/Water System(2004)