Biodegradable Pectin/Clay Aerogels
Citations Over TimeTop 10% of 2013 papers
Abstract
Biodegradable, foamlike materials based on renewable pectin and sodium montmorillonite clay were fabricated through a simple, environmentally friendly freeze-drying process. The addition of multivalent cations (Ca(2+) and Al(3+)) resulted in apparent cross-linking of the polymer and enhancement of aerogel properties. The compressive properties increased as the solid contents (both pectin and clay) increased; moduli in the range of 0.04-114 MPa were obtained for materials with bulk densities ranging from 0.03 g/cm(3) to 0.19 g/cm(3), accompanied by microstructural changes from a lamellar structure to a cellular structure. Biodegradability of the aerogels was investigated by detecting CO2 release for 4 weeks in compost media. The results revealed that pectin aerogels possess higher biodegradation rates than wheat starch, which is often used as a standard for effective biodegradation. The addition of clay and multivalent cations surprisingly increased the biodegradation rates.
Related Papers
- → Current status, opportunities, and challenges in fuel cell catalytic application of aerogels(2019)44 cited
- → Synthesis of aerogel foams through a pressurized sol-gel method(2020)18 cited
- → Utilization of aerogel in building construction –A Review(2020)19 cited
- → Effect of processing parameters and pore structure of nanostructured silica aerogel on the physical properties of aerogel blankets(2018)8 cited
- Aerogel + Aerogel = Aerogel²Developments on Aerogel-Aerogel Composites(2011)