Enhanced Photoelectrochemical Water Splitting Performance of Anodic TiO₂Nanotube Arrays by Surface Passivation

Citations Over TimeTop 10% of 2014 papers

Abstract

One-dimensional anodic titanium oxide nanotube (TONT) arrays provide a direct pathway for charge transport, and thus hold great potential as working electrodes for electrochemical energy conversion and storage devices. However, the prominent surface recombination due to the large amount surface defects hinders the performance improvement. In this work, the surface states of TONTs were passivated by conformal coating of high-quality Al2O3 onto the tubular structures using atomic layer deposition (ALD). The modified TONT films were subsequently employed as anodes for photoelectrochemical (PEC) water splitting. The photocurrent (0.5 V vs Ag/AgCl) recorded under air mass 1.5 global illumination presented 0.8 times enhancement on the electrode with passivation coating. The reduction of surface recombination rate is responsible for the substantially improved performance, which is proposed to have originated from a decreased interface defect density in combination with a field-effect passivation induced by a negative fixed charge in the Al2O3 shells. These results not only provide a physical insight into the passivation effect, but also can be utilized as a guideline to design other energy conversion devices.

Related Papers

• → Fabrication of an Efficient BaTaO₂N Photoanode Harvesting a Wide Range of Visible Light for Water Splitting(2013)224 cited
• → Hierarchically branched Fe₂O₃@TiO₂nanorod arrays for photoelectrochemical water splitting: facile synthesis and enhanced photoelectrochemical performance(2016)92 cited
• → Photoelectrochemical Properties and Behavior of α-SnWO₄ Photoanodes Synthesized by Hydrothermal Conversion of WO₃ Films(2016)49 cited
• → Semiconductive properties and photoelectrochemistry of an iron oxide electrode—VII. Photoresponse observed in initial pitting period of iron passive film in acidic medium(1989)6 cited
• → Reply to Comment on “Commercially Available WO₃ Nanopowders for Photoelectrochemical Water Splitting: Photocurrent versus Oxygen Evolution”(2017)