Water-Induced Degradation of Polymer Solar Cells Studied by H₂18O Labeling

Citations Over TimeTop 1% of 2008 papers

Abstract

Water-induced degradation of polymer photovoltaics based on the active materials poly(3-hexylthiophene) (P3HT) or poly[2-methoxy-5-(2'-ethylhexyloxy)-1,4-phenylenevinylene] (MEHPPV) was studied. The solar cell devices comprised a bulk heterojunction formed by the active material and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) in a standard device geometry. The use of H2(18)O in conjunction with time-of-flight secondary ion mass spectrometry enabled mapping of the parts of the device that were induced by water. A comparison was made between the two active materials and between devices that were kept in the dark and devices that had been subjected to illumination under simulated sunlight. Devices that were exposed to ambient humidity were compared to devices exposed to saturated humidity. Finally, a comparison was made between results obtained using H2(18)O and earlier work involving 18O2. Water was found to have behavior similar to but not identical with molecular oxygen.

Related Papers

• → Effect of relative humidity on thermal degradation of Norway spruce (Picea abies) wood(2008)54 cited
• → Characterization of polymer–fullerene mixtures for organic photovoltaics by systematically coarse-grained molecular simulations(2010)54 cited
• → Improved quantification in secondary-ion mass spectrometry detecting MCs+ molecular ions(1994)61 cited
• → Accelerated stability testing of organic photovoltaics using concentrated sunlight(2012)4 cited
• → SIMS measurements of oxygen content in the Nd2Fe14B phase(2005)7 cited