Thermal Degradation of Poly(3-hydroxyalkanoates): Preparation of Well-Defined Oligomers

Citations Over TimeTop 15% of 2001 papers

Abstract

The thermal degradation of the biodegradable bacterial polyesters poly(3-hydroxybutyrate), PHB, poly(3-hydroxyvalerate), PHV, and poly(3-hydroxybutyrate-co-3-hydroxyvalerate), 0-21 mol % of hydroxyvalerate, was studied. At moderately low temperatures (170-200 degrees C), the main product is a well-defined oligomer, especially a 500-10,000 g/mol macromolecule, which contains one unsaturated end group, predominantly a trans-alkenyl end group, as well as a carboxylic end group. The process was studied regarding the effect of the copolymer composition and reaction time at 190 degrees C. During the first few hours of reaction, the thermal degradation of PHB and PHV followed a kinetic model of random scission, but eventually auto-acceleration of the pyrolysis was detected, probably due to the influence of the crotonate end groups of the oligomers formed. Ten-time scale-up experiments on a Brabender instrument were successfully undertaken.

Related Papers

• → Solution Structure of Apoptotic BAX Oligomer: Oligomerization Likely Precedes Membrane Insertion(2015)48 cited
• → Elucidating Oligomer-Surface and Oligomer-Oligomer Interactions at a Lithiated Silicon Surface(2016)10 cited
• → Case study on the evolution of hetero-oligomer interfaces based on the differences in paralogous proteins(2015)4 cited
• → The Historical Development of Polyesters(2004)19 cited
• Application research review of Polyesters in FPC(2010)