Periodic Disorder along Ramie Cellulose Microfibrils

Citations Over TimeTop 10% of 2003 papers

Abstract

Small angle neutron scattering studies have been carried out on cellulose fibers from ramie and Populus maximowicii (cotton wood). Labile hydrogen atoms were replaced by deuterium atoms, in water-accessible disordered regions of the fibers, to increase the neutron scattering contrast between the disordered and crystalline regions. A meridional Bragg reflection, corresponding to a longitudinal periodicity of 150 nm, was observed when scattering collected from hydrogenated and deuterated dry ramie fibers was subtracted. No Bragg reflection was observed with the cotton wood fibers, probably because of lower orientation of the microfibrils in the cell wall. The ramie fibers were then subjected to electron microscopy, acid hydrolysis, gel permeation chromatography, and viscosity studies. The leveling off degree of polymerization (LODP) of the hydrolyzed samples matched exactly the periodicity observed in the diffraction studies. The weight loss related to the LODP was only about 1.5%, and thus, the microfibrils can be considered to have 4-5 disordered residues every 300 residues.

Related Papers

• → Re-constructing our models of cellulose and primary cell wall assembly(2014)436 cited
• → Crystalline and amorphous cellulose in the secondary walls of Arabidopsis(2012)87 cited
• → Vibrational sum-frequency-generation (SFG) spectroscopy study of the structural assembly of cellulose microfibrils in reaction woods(2014)37 cited
• → Structural diversity of natural cellulose and related applications using delignified wood(2022)10 cited
• → Preparation, Properties and Chemical Modification of Nanosized Cellulose Fibrils(2008)2 cited