Coalesced Poly(ε-caprolactone) Fibers Are Stronger

Citations Over TimeTop 15% of 2015 papers

Abstract

Melt-spun fibers were made from poly(ε-caprolactone) (PCL) coalesced from stoichiometric inclusion complex crystals formed with host urea. Melting and crystallization behaviors, mechanical properties, and the birefringence of undrawn and cold-drawn fibers were investigated. Undrawn coalesced PCL fibers were observed to have 500-600% higher moduli than undrawn as-received (asr) PCL fibers and a modulus comparable to drawn asr PCL fibers. Drawn coalesced PCL fibers have the highest crystallinity, orientation, and 65% higher moduli than drawn asr PCL fibers. Drawn coalesced PCL fibers have only a 5% higher crystallinity than drawn asr PCL fibers, yet they have 65% higher moduli and lower elongation at break values. Clearly, the intrinsic alignment of the coalesced polymers is the reason for their higher moduli and lower elongation, as confirmed by the birefringence observed in drawn coalesced and asr-PCL fibers. The improved mechanical properties of coalesced PCL fibers make them a better candidate for use in tissue engineering as scaffolds.

Related Papers

• → X-ray diffraction and infrared spectroscopy analyses on the crystallinity of engineered biological hydroxyapatite for medical application(2015)83 cited
• → Influence of antioxidants and cross-linking on the crystallinity of XLPE dielectrics(2007)8 cited
• → A Comparative Study of The Crystallinity Value of Polyethylene Glycol-Based Composites Using XRD and WAXS(2022)4 cited
• → The effect of the conditions of the treatment of gel on the crystallinity of the layered compound zirconium (IV) BIS(phosphite)(1990)3 cited
• Research on Crystallization Behavior of PVF Film during Processing(2008)