Preparation and Growth Mechanism of Gold Nanorods (NRs) Using Seed-Mediated Growth Method
Citations Over TimeTop 1% of 2003 papers
Abstract
A method is used for preparing gold NRs with aspect ratios ranging from 1.5 to 10 for which the surface plasmon absorption maxima are between 600 and 1300 nm. This method has been adapted from a previously published seed-mediated growth method (Jana et al. Adv. Mater. 2001, 13, 1389). The disadvantages and limitations of the earlier method (i.e., formation of noncylindrical NRs, φ-shaped particles, and formation of a large fraction of spherical particles) have been overcome by use of a hexadecyltrimethylammonium bromide (CTAB)-capped seed instead of a citrate-capped one. In a single-component surfactant system, the silver content of the growth solution was used to grow NRs to a desired length. This results in reproducible formation of NRs with aspect ratios ranging from 1.5 to 4.5. To grow longer NRs with aspect ratios ranging from 4.6 to 10, a binary surfactant mixture composed of benzyldimethylhexadecylammoniumchloride (BDAC) and CTAB was used. NRs are grown in this mixture either by aging or by addition of a growth solution suitable to shorter NRs. Effects of the silver ion and the cosurfactant along with the growth mechanism of NRs are discussed.
Related Papers
- → Stability and Transformations of Heated Gold Nanorods(2011)30 cited
- → Single crystal TiO2 nanorods: Large-scale synthesis and field emission(2012)18 cited
- → Size-dependent water splitting activity of ZnO nanorods(2019)3 cited
- → Superfocusing effect in the chain of silver nanorods(2011)2 cited
- Solvothermal Synthesis of CdSxSe1-x Nanorods by Polymer Gel-Controlled Growth Strategy(2007)