Melilite-Type Borates Bi2ZnB2O7 and CaBiGaB2O7
Citations Over TimeTop 13% of 2005 papers
Abstract
The bismuth borates Bi2ZnB2O7 and CaBiGaB2O7 have been synthesized by solid-state reactions at temperatures in the 650−825 °C range at 1 atm pressure. These compounds are the only synthetic diborate members of the melilite family, A2XZ2O7, in which layers of A cations alternate with XZ2O7 tetrahedral layers. Except for CdBiGaB2O7, the synthesis of other substituted bismuth borate melilites has been unsuccessful. The crystal structures of Bi2ZnB2O7 and CaBiGaB2O7 have been determined by powder X-ray diffraction and refined by the Rietveld method using powder neutron diffraction data. CaBiGaB2O7 adopts the regular tetragonal melilite structure (P4̄21m space group, Z = 2) containing B2O7 tetrahedral dimers. The refinement of split eight-coordinated sites for the Ca2+ and Bi3+ interlayer cations suggests the presence of additional disorder. Bi2ZnB2O7 adopts a unique orthorhombic melilite superstructure (Pba2 space group, Z = 4) containing both tetrahedral B2O7 and triangular B2O5 dimers. The Bi3+ cations occupy two distinct interlayer sites with strongly asymmetric 6-fold coordination environments. The preliminary measurement of second harmonic generation efficiencies (deff) of powder samples has yielded values of 4.0 (Bi2ZnB2O7) and 1.6 (CaBiGaB2O7) relative to a KH2PO4 standard.
Related Papers
- → Rietveld Refinement for Macromolecular Powder Diffraction(2020)17 cited
- → Rietveld refinement of several structural models for mordenite that account for differences in the X-ray powder pattern(1994)32 cited
- → Identification and characterisation of thaumasite by XRPD techniques(1999)17 cited
- → Rietveld refinement of the semiconducting compound CdGaCrS4 from X-ray powder diffraction(2003)3 cited
- → Restrained Rietveld refinement of molecular materials followingab-initiostructure solution from powder diffraction data(2002)