Poly(methacrylic acid) Hydrogel Films and Capsules: Response to pH and Ionic Strength, and Encapsulation of Macromolecules

Citations Over TimeTop 10% of 2005 papers

Abstract

Hydrogen-bonded multilayers of a neutral polymer (poly(N-vinylpyrrolidone), PVPON) with poly(methacrylic acid) (PMAA) were used as templates to introduce cross-links between PMAA layers using carbodiimide chemistry and ethylenediamine as a cross-linking agent. Upon exposure to high pH, PVPON is completely released from the hydrogel matrix, producing surface-attached PMAA hydrogels. When such hydrogels are deposited at the surface of silica particles, and the particle core is subsequently dissolved, hollow one-component hydrogel capsules are produced. PMAA hydrogel films and hollow capsules underwent reversible, large (factors of 2 or 3) changes in size in response to changes in solution pH and/or ionic strength. The capsules were used for entrapment and storage of macromolecules such as 500 kDa FITC-dextran by “locking” the capsule wall with an electrostatically associating polycation, poly-N-ethyl-4-vinylpyridinium bromide (QPVP). The release of the encapsulated macromolecules was achieved under high salt concentrations (0.6 M NaCl) when QPVP dissociated from the capsule wall. The pH and salt response of these PMAA hydrogel capsules and the polycation-controlled encapsulation of macromolecules hold promise for applications in biomedicine and biotechnology.

Related Papers

• → Synthesis, characterization and swelling behaviour of poly(methacrylic acid) brushes synthesized using atom transfer radical polymerization(2008)85 cited
• → Interaction between Methylene Blue and Cyclic Methacrylic Acid Oligomer(2007)9 cited
• → Aldehyde–dextran–protein conjugates to immobilize amino-haptens: avoiding cross-reactions in the immunodetection(2004)12 cited
• → Fluorescence probe studies on the complexation between poly(methacrylic acid) and poly(N, N-diethylacrylamide)(2004)7 cited
• Complex Formation of Syndiotactic Poly(methacrylic acid) with Complementary Polymers through Hydrogen Bonding(1986)