Nanosilicon Electrodes for Lithium-Ion Batteries: Interfacial Mechanisms Studied by Hard and Soft X-ray Photoelectron Spectroscopy

Citations Over TimeTop 1% of 2012 papers

Abstract

Largely based on its very high rechargeable capacity, silicon appears as an ideal candidate for the next generation of negative electrodes for Li-ion batteries. However, a crucial problem with silicon is the large volume expansion undergone upon alloying with lithium, which results in stability problems. Means to avoid such problems are largely linked to the understanding of the interfacial chemistry during charging/discharging. This is especially of great importance when using nanometric silicon particles. In this work, the interfacial mechanisms (reaction of surface oxide, Li–Si alloying process, and passivation layer formation) accompanying lithium insertion/extraction into Si/C/CMC composite electrodes have been scrutinized by X-ray photoelectron spectroscopy (XPS). A thorough nondestructive depth-resolved analysis was carried out by using both soft X-rays (100–800 eV) and hard X-rays (2000–7000 eV) from two different synchrotron facilities compared with in-house XPS (1487 eV). The unique combination utilizing hard and soft X-ray photoelectron spectroscopy accompanied with variation of the analysis depth allowed us to access interfacial phase transitions at the surface of silicon particles as well as the composition and thickness of the SEI (electrode/electrolyte interface layer).

Related Papers

• → Passivation and Surface Film Formation(1996)7 cited
• → Elimination of parasitic effects in floating junction rear surface passivation for solar cells(1996)17 cited
• → Sulfur passivation of 3C-SiC thin film(2018)4 cited
• Development of High Performance Chromium-Free Passivation Agent Suitable for Coating of Aluminum Alloy and Optimization of Passivation Technology(2012)
• Passivation method of 317L stainless steel used in medicine(2002)