Anisotropic Oxygen Ion Diffusion in Layered PrBaCo2O5+δ
Citations Over TimeTop 10% of 2012 papers
Abstract
Oxygen diffusion and surface exchange coefficients have been measured on polycrystalline samples of the double perovskite oxide PrBaCo2O5+δ by the isotope exchange depth profile method, using a time-of-flight SIMS instrument. The measured diffusion coefficients show an activation energy of 1.02 eV, as compared to 0.89 eV for the surface exchange coefficients in the temperature range from 300 to 670 °C. Inhomogeneity was observed in the distribution of the oxygen-18 isotopic fraction from grain to grain in the ceramic samples, which was attributed to anisotropy in the diffusion and exchange of oxygen. By the use of a novel combination of electron back scattered diffraction measurements, time-of-flight, and focused ion beam SIMS, this anisotropy was confirmed by in-depth analysis of single grains of known orientation in a ceramic sample exchanged at 300 °C. Diffusion was shown to be faster in a grain oriented with the surface normal close to 100 and 010 (ab-plane oriented) than a grain with a surface normal close to 001 (c-axis oriented). The magnitude of this anisotropy is estimated to be close to a factor of 4, but this is only a lower bound due to experimental limitations. These findings are consistent with recent molecular dynamic simulations of this material where anisotropy in the oxygen transport was predicted.
Related Papers
- → Growth of Hydrothermally Derived CdS-Based Nanostructures with Various Crystal Features and Photoactivated Properties(2016)38 cited
- → Crystallite damage studies on irradiated poly(vinylidene fluoride)(1994)19 cited
- → Role of the KBr surfaces in crystallization of poly(vinylidene fluoride) films with a KBr powder as a nucleating agent(2014)18 cited
- → An investigation of crystallite alignment and polymorphic interaction of glutamic acid using an in situ synchrotron X-ray diffraction tomographic technique(2006)6 cited
- Optical Property of FeVO_4 Crystallites Synthesized by Sonochemical Method(2012)