Oxidation-Induced Trapping of Drugs in Porous Silicon Microparticles

Citations Over TimeTop 10% of 2014 papers

Abstract

An approach for the preparation of an oxidized porous silicon microparticle drug delivery system that can provide efficient trapping and sustained release of various drugs is reported. The method uses the contraction of porous silicon's mesopores, which occurs during oxidation of the silicon matrix, to increase the loading and retention of drugs within the particles. First, a porous Si (pSi) film is prepared by electrochemical etching of p-type silicon with a resistivity of >0.65 Ω cm in a 1:1 (v/v) HF/ethanol electrolyte solution. Under these conditions, the pore walls are sufficiently thin to allow for complete oxidation of the silicon skeleton under mild conditions. The pSi film is then soaked in an aqueous solution containing the drug (cobinamide or rhodamine B test molecules were used in this study) and sodium nitrite. Oxidation of the porous host by nitrite results in a shrinking of the pore openings, which physically traps the drug in the porous matrix. The film is subsequently fractured by ultrasonication into microparticles. Upon comparison with commonly used oxidizing agents for pSi such as water, peroxide, and dimethyl sulfoxide, nitrite is kinetically and thermodynamically sufficient to oxidize the pore walls of the pSi matrix, precluding reductive (by Si) or oxidative (by nitrite) degradation of the drug payload. The drug loading efficiency is significantly increased (by up to 10-fold), and the release rate is significantly prolonged (by 20-fold) relative to control samples in which the drug is loaded by infiltration of pSi particles postoxidation. We find that it is important that the silicon skeleton be completely oxidized to ensure the drug is not reduced or degraded by contact with elemental silicon during the particle dissolution-drug release phase.

Related Papers

• → The drastic effect of oxygen on surface segregation(1990)2 cited
• → Reducing action of persulfuric acid(1967)
• Complex Properties of Black Wattle Extract and Its Oxidizing Modified Products Reacting With Cr(III)(2002)
• Improvement in protection character of conductive chemical oxidizing film(2004)
• → The Corrosion of Aluminum and Its Alloy Caused by Addition of Acid, Alkali, Oxidizing Agents and Reducing Agents(1962)