Tailoring the Structure of Thin Film Nanocomposite Membranes to Achieve Seawater RO Membrane Performance
Citations Over TimeTop 10% of 2010 papers
Abstract
Herein we report on the formation and characterization of pure polyamide thin film composite (TFC) and zeolite-polyamide thin film nanocomposite (TFN) reverse osmosis (RO) membranes. Four different physical-chemical post-treatment combinations were applied after the interfacial polymerization reaction to change the molecular structure of polyamide and zeolite-polyamide thin films. Both TFC and TFN hand-cast membranes were more permeable, hydrophilic, and rough than a commercial seawater RO membrane. Salt rejection by TFN membranes was consistently below that of hand-cast TFC membranes; however, two TFN membranes exhibited 32 g/L NaCl rejections above 99.4%, which was better than the commercial membrane under the test conditions employed. The nearly defect-free TFN films that produced such high rejections were achieved only with wet curing, regardless of other post-treatments. Polyamide films formed in the presence of zeolite nanoparticles were less cross-linked than similarly cast pure polyamide films. At the very low nanoparticle loadings evaluated, differences between pure polyamide and zeolite-polyamide membrane water and salt permeability correlated weakly with extent of cross-linking of the polyamide film, which suggests that defects and molecular-sieving largely govern transport through zeolite-polyamide thin film nanocomposite membranes.
Related Papers
- → Regulating the interfacial polymerization process toward high-performance polyamide thin-film composite reverse osmosis and nanofiltration membranes: A review(2021)261 cited
- → Influence of l-arginine on performances of polyamide thin-film composite reverse osmosis membranes(2019)27 cited
- → Truly chlorine-resistant polyamide reverse osmosis composite membrane(1996)10 cited
- Interfacially synthesized thin-film composite reverse osmosis membranes and their surface modification(2011)
- → Truly chlorine‐resistant polyamide reverse osmosis composite membrane(1996)