Effect of Impurities on the Corrosion Behavior of CO₂ Transmission Pipeline Steel in Supercritical CO₂−Water Environments

Citations Over TimeTop 10% of 2010 papers

Abstract

The corrosion property of carbon steel was evaluated using an autoclave under CO(2)-saturated water phase and water-saturated CO(2) phase with impurities (O(2) and SO(2)) at 80 bar CO(2) and 50 °C to simulate the condition of CO(2) transmission pipeline in the carbon capture and storage (CCS) applications. The results showed that the corrosion rate of carbon steel in CO(2)-saturated water was very high and it increased with adding O(2) in the system due to the inhibition effect of O(2) on the formation of protective FeCO(3). It is noteworthy that corrosion took place in the water-saturated CO(2) phase under supercritical condition when no free water is present. The addition of O(2) increased the corrosion rates of carbon steel in water-saturated CO(2) phase. The addition of 0.8 bar SO(2) (1%) in the gas phase dramatically increased the corrosion rate of carbon steel from 0.38 to 5.6 mm/y. This then increased to more than 7 mm/y with addition of both O(2) and SO(2). SO(2) can promote the formation of iron sulfite hydrate (FeSO(3)·3H(2)O) on the steel surface which is less protective than iron carbonate (FeCO(3)), and it is further oxidized to become FeSO(4) and FeOOH when O(2) is present with SO(2) in the CO(2)-rich phase. The corrosion rates of 13Cr steel were very low compared with carbon steel in CO(2)-saturated water environments with O(2), whereas it was as high as carbon steel in a water-saturated CO(2) phase with O(2) and SO(2).

Related Papers

• → Effects of heat-stable salts on the corrosion behaviours of 20 steel in the MDEA/H₂S/CO₂ environment(2019)20 cited
• → Supercritical phases of hydrogen(2021)14 cited
• Preparation of Microparticles with Supercritical Solution Precipitation Technology(2005)
• Progress in Formation of Ultrafine Powder by Supercritical Fluid(2008)