Thin-Film Composite Pressure Retarded Osmosis Membranes for Sustainable Power Generation from Salinity Gradients

Citations Over TimeTop 1% of 2011 papers

Abstract

Pressure retarded osmosis has the potential to produce renewable energy from natural salinity gradients. This work presents the fabrication of thin-film composite membranes customized for high performance in pressure retarded osmosis. We also present the development of a theoretical model to predict the water flux in pressure retarded osmosis, from which we can predict the power density that can be achieved by a membrane. The model is the first to incorporate external concentration polarization, a performance limiting phenomenon that becomes significant for high-performance membranes. The fabricated membranes consist of a selective polyamide layer formed by interfacial polymerization on top of a polysulfone support layer made by phase separation. The highly porous support layer (structural parameter S = 349 μm), which minimizes internal concentration polarization, allows the transport properties of the active layer to be customized to enhance PRO performance. It is shown that a hand-cast membrane that balances permeability and selectivity (A = 5.81 L m(-2) h(-1) bar(-1), B = 0.88 L m(-2) h(-1)) is projected to achieve the highest potential peak power density of 10.0 W/m(2) for a river water feed solution and seawater draw solution. The outstanding performance of this membrane is attributed to the high water permeability of the active layer, coupled with a moderate salt permeability and the ability of the support layer to suppress the undesirable accumulation of leaked salt in the porous support. Membranes with greater selectivity (i.e., lower salt permeability, B = 0.16 L m(-2) h(-1)) suffered from a lower water permeability (A = 1.74 L m(-2) h(-1) bar(-1)) and would yield a lower peak power density of 6.1 W/m(2), while membranes with a higher permeability and lower selectivity (A = 7.55 L m(-2) h(-1) bar(-1), B = 5.45 L m(-2) h(-1)) performed poorly due to severe reverse salt permeation, resulting in a similar projected peak power density of 6.1 W/m(2).

Related Papers

• → Performance Limiting Effects in Power Generation from Salinity Gradients by Pressure Retarded Osmosis(2011)328 cited
• → Enhanced osmotic energy generation from salinity gradients by modifying thin film composite membranes(2014)147 cited
• → Preparation, characterization and performance evaluations of thin film composite hollow fiber membrane for energy generation(2014)48 cited
• → Water and Salt Fluxes in Pressure Retarded Osmosis(2017)4 cited
• → Membrane Development for Pressure-Retarded Osmosis(2015)3 cited