Molecular Insights of Oxidation Process of Iron Nanoparticles: Spectroscopic, Magnetic, and Microscopic Evidence
Citations Over TimeTop 10% of 2014 papers
Abstract
Oxidation behavior of nano-Fe(0) particles in an anoxic environment was determined using different state-of-the-art analytical approaches, including high resolution transmission electron microscopy (HR-TEM) combined with energy filtered transmission electron microscopy (EFTEM), X-ray absorption spectroscopy (XAS), and magnetic measurements. Oxidation in controlled experiments was compared in standard double distilled (DD) water, DD water spiked with trichloroethene (TCE), and TCE contaminated site water. Using HR-TEM and EFTEM, we observed a surface oxide layer (∼3 nm) formed immediately after the particles were exposed to water. XAS analysis followed the dynamic change in total metallic iron concentration and iron oxide concentration for the experimental duration of 35 days. The metallic iron concentration in nano-Fe(0) particles exposed to water, was ∼40% after 35 days; in contrast, the samples containing TCE were reduced to ∼15% and even to nil in the case of TCE contaminated site water, suggesting that the contaminants enhance the oxidation of nano-Fe(0). Frequency dependence measurements confirmed the formation of superparamagnetic particles in the system. Overall, our results suggest that nano-Fe(0) oxidized via the Fe(0) - Fe(OH)2 - Fe3O4 - (γ-Fe2O3) route and the formation of superparamagnetic maghemite nanoparticles due to disruption of the surface oxide layer.
Related Papers
- → Characterizing the protein corona of sub-10 nm nanoparticles(2019)53 cited
- → Exploiting nanoparticles as precursors for novel nanostructure designs and properties(2012)30 cited
- → Fabrication and characterization of Pd Nanoparticles(2006)18 cited
- Carbon encapsulated magnetic nanoparticles produced by hydrothermal reaction(2007)
- Structure and Magnetic Properties of S-doped Mn_3O_4/S Composited Nanoparticles and Mn_3O_4 Nanoparticles(2011)