Phase Progression of γ-Al2O3 Nanoparticles Synthesized in a Solvent-Deficient Environment
Citations Over TimeTop 16% of 2013 papers
Abstract
Our simple and uniquely cost-effective solvent-deficient synthetic method produces 3-5 nm Al2O3 nanoparticles which show promise as improved industrial catalyst-supports. While catalytic applications are sensitive to the details of the atomic structure, a diffraction analysis of alumina nanoparticles is challenging because of extreme size/microstrain-related peak broadening and the similarity of the diffraction patterns of various transitional Al2O3 phases. Here, we employ a combination of X-ray pair-distribution function (PDF) and Rietveld methods, together with solid-state NMR and thermogravimetry/differential thermal analysis-mass spectrometry (TG/DTA-MS), to characterize the alumina phase-progression in our nanoparticles as a function of calcination temperature between 300 and 1200 °C. In the solvent-deficient synthetic environment, a boehmite precursor phase forms which transitions to γ-Al2O3 at an extraordinarily low temperature (below 300 °C), but this γ-Al2O3 is initially riddled with boehmite-like stacking-fault defects that steadily disappear during calcination in the range from 300 to 950 °C. The healing of these defects accounts for many of the most interesting and widely reported properties of the γ-phase.
Related Papers
- → Differential Thermogravimetry(1954)32 cited
- → Thermal characterization of some azo dyes containing intermolecular hydrogen bonds and non-bonds(2003)15 cited
- → Thermal analysis of pharmaceutical compounds(1981)15 cited
- Research on Optimal Characterization Method of CaC_2O_4·H_2O by Thermogravimetry-Differential Thermal Analyzer(2011)
- → Thermal analysis of N-phenylbenzohydroxamic acid (PBHA)(1978)1 cited