Magnetic Properties and Negative Colossal Magnetoresistance of the Rare Earth Zintl phase EuIn2As2
Citations Over TimeTop 13% of 2008 papers
Abstract
Large, high quality single crystals of a new Zintl phase, EuIn(2)As(2), have been synthesized from a reactive indium flux. EuIn(2)As(2) is isostructural to the recently reported phase EuIn(2)P(2), and it is only the second reported member of the group of compounds with formula AM(2)X(2) (A = alkali, alkaline earth, or rare earth cation; M = transition or post-transition metal; and X = Group 14 or 15 element) that crystallizes in the hexagonal space group P6(3)/mmc (a = 4.2067(3) A, c = 17.889(2) A and Z = 2). The structure type contains layers of A(2+) cations separated by [M(2)X(2)](2-) layers along the crystallographic c-axis. Crystals of the title compound were mounted for magnetic measurements, with the crystallographic c-axis oriented either parallel or perpendicular to the direction of the applied field. The collective magnetization versus temperature and field data indicate two magnetic exchange interactions near 16 K, one involving Eu(2+)...Eu(2+) intralayer coupling and the other involving Eu(2+)...Eu(2+) coupling between layers. EuIn(2)As(2) is metallic and magnetoresistive, as is the isostructural phosphide, and both compounds have coincident resistivity and magnetic ordering transitions, consistent with the observation of colossal magnetoresistance. Negative colossal magnetoresistance (MR = {[rho(H) - rho(0)]/rho(H)} x 100%) of up to -143% (at T = 17.5 K, H = 5 T) is observed for EuIn(2)As(2), approximately half of that observed for the more resistive phosphide, which has a higher magnetic ordering temperature and local moment coupling strength.
Related Papers
- → Room Temperature Magnetoresistance at Low Magnetic Fields in La0.7 Ba0.3 MnO3(2000)6 cited
- → Controlled temperature broadening of colossal magnetoresistance in a manganite heterostructure(1997)3 cited
- Magnetoresistance effects in granular rare-earth doped oxides(2003)
- Colossal Magnetoresistance Effect ofLa_(0.67)Ca_(0.33)Mn_(1-x)T_xO_3 under Low Magnetic Fields(2001)