Preparation of Zeolite ZSM-5 Membranes by In-Situ Crystallization on Porous .alpha.-Al2O3

Citations Over TimeTop 1% of 1995 papers

Abstract

Zeolite ZSM-5 membranes were grown on porous α-Al_2O_3 disks by in-situ hydrothermal synthesis at 175 "C. The zeolite layers were formed on the bottom face of disks placed horizontally near the air-liquid interface of clear synthesis solutions. Extensive experimentation was carried out to find compositions that gave continuous polycrystalline films. The films grown with the optimized composition were about 10 µm thick and consisted of well-intergrown crystals of about 2 µm size. Pure gas permeation measurements of the most successful preparation yielded hydrogen:isobutane and n-butane:isobutane ratios of 151 and 18 at room temperature and 54 and 31 at 185 °C, respectively.

Related Papers

• → Fast and efficient synthesis of SSZ-13 by interzeolite conversion of Zeolite Beta and Zeolite L(2019)65 cited
• Research Progress of zeolite synthesis from kaolin(2010)
• Polysulfone으로 제올라이트 A를 고정화한 방사성 물질제거용 PS-zeolite 비드 제조(2015)
• 쳔연 Zeolite ( 제올라이트 ) 를 이용한 중금속 흡착제의 개발(1991)
• Crystallization of Zeolite A and HS and Conversion of Zeolite A into Zeolite HS(1988)