Effects of Boron Doping on Photocatalytic Activity and Microstructure of Titanium Dioxide Nanoparticles

Citations Over TimeTop 1% of 2006 papers

Abstract

Boron-doped TiO2 nanoparticles were prepared by the sol−gel method and characterized by XRD, TEM, XPS, FT-IR, and UV−vis spectroscopy. XRD results showed that the doping of boron ions could efficiently inhibit the grain growth and facilitate the anatase-to-rutile transformation prior to the formation of diboron trioxide phase. FT-IR and XPS results revealed that the doped boron was present as the form of B3+ in B-doped TiO2 samples, forming a possible chemical environment like Ti−O−B. The lattice parameters at different boron contents and calcination temperatures indicated that B3+ was likely to weave into the interstitial TiO2 structure. The photocatalytic activity of the B-doped TiO2 nanoparticles was evaluated by the photoregeneration of reduced nicotinamide adenine dinucleotide (NADH). All B-doped TiO2 nanoparticles calcined at 500 °C showed higher photocatalytic activity than pure TiO2 sample in the photocatalytic reaction of NADH regeneration under UV light irradiation. When the molar ratio of B to Ti was 5%, the TiO2 nanoparticles could photocatalytically reproduce 94% NADH.

Related Papers

• → The role of the surface intermediates in the photoelectrochemical behaviour of anatase and rutile TiO2(1993)240 cited
• → Photodegradation of organic dyes based on anatase and rutile TiO₂nanoparticles(2015)150 cited
• → Electrostatic potential calculations on crystalline TiO2: The surface reducibility of rutile and anatase(1983)33 cited
• → Infrared– active defects in a TiO2 mixture of coexisting anatase and rutile phases(2003)19 cited
• → 주형합성을 통한 메조포러스 TiO 2 제조 및 실리카 메조포어 내부에서의 TiO 2 상전이 거동 변화(2018)