Change of CO2Carrying Capacity of CaO in Isothermal Recarbonation−Decomposition Cycles
Citations Over TimeTop 1% of 2007 papers
Abstract
The change of CO2 carrying capacity of CaO sorbents prepared from different precursors has been studied using thermogravimetric analysis in a long series of isothermal recarbonation−decomposition cycles in the temperature range of 750−850 °C. The residual capacity of the CaO sorbents after a large number of cycles was found to depend on the precursor type, the experimental temperature, and the duration of the recarbonation stage. The residual capacities of the CaO derived from the powdered calcium carbonates were much higher than that of the CaO produced from the crystalline CaCO3. A simple tentative model has been suggested, according to which recarbonation−decomposition cycles result in formation of the interconnected CaO network that acts as a refractory support and determines sorption properties of the material. By using a new model, a simple synthesis procedure has been suggested that produces CaO sorbents with high residual CO2 carrying capacities.
Related Papers
- → The use of thermogravimetric analysis technique for the characterization of construction materials(2008)77 cited
- → Kinetic analysis of thermogravimetric data on some nickel(II) N-alkyldithiocarbamates(1989)25 cited
- → Thermogravimetric analysis for the characterization and comparative analysis of polyvinyl chloride (PVC) wall panel(2023)1 cited
- → A critical reflection upon the application of the Arrhenius model to non-isothermal thermogravimetric curves(1982)41 cited
- → Dynamic and isothermal thermogravimetric analysis of a polycyanurate thermosetting system(1998)11 cited