Platinum-Containing Hyper-Cross-Linked Polystyrene as a Modifier-Free Selective Catalyst for l-Sorbose Oxidation

Citations Over TimeTop 10% of 2001 papers

Abstract

Impregnation of hyper-cross-linked polystyrene (HPS) with tetrahydrofuran (THF) or methanol (ML) solutions containing platinic acid results in the formation of Pt(II) complexes within the nanocavities of HPS. Subsequent reduction of the complexes by H2 yields stable Pt nanoparticles with a mean diameter of 1.3 nm in THF and 1.4 nm in ML. The highest selectivity (98% at 100% conversion) measured during the catalytic oxidation of L-sorbose in water is obtained with the HPS-Pt-THF complex prior to H2 reduction. During an induction period of about 100 min, L-sorbose conversion is negligible while catalytic species develop in situ. The structure of the catalyst isolated after the induction period is analyzed by X-ray diffraction, transmission electron microscopy, and X-ray photoelectron spectroscopy. Electron micrographs reveal a broad distribution of Pt nanoparticles, 71% of which measure less than or equal to 2.0 nm in diameter. These nanoparticles are most likely responsible for the high catalytic activity and selectivity observed. The formation of nanoparticles measuring up to 5.9 nm in diameter is attributed to the facilitated intercavity transport and aggregation of smaller nanoparticles in swollen HPS. The catalytic properties of these novel Pt nanoparticles are highly robust, remaining stable even after 15 repeated uses.

Related Papers

• → HxMoO3-assisted deposition of platinum nanoparticles on MWNTs for electrocatalytic oxidation of methanol(2011)18 cited
• → Hydridosilsesquioxane Modified Silica-Supported Platinum Nanoparticles(1996)21 cited
• Effect of solution acidity on methanol oxidation for platinum electrode(2005)
• Electrooxidation of Methanol on the Platinum Nanoparticles Modified Platinum Electrode(2007)
• Utilising solution dispersed platinum nanoparticles to direct the growth of electrodeposited platinum nanostructures and its influence on the electrocatalytic oxidation of small organic molecules(2016)