Engineering InAsxP1-x/InP/ZnSe III−V Alloyed Core/Shell Quantum Dots for the Near-Infrared
Citations Over TimeTop 10% of 2005 papers
Abstract
Quantum dots with a core/shell/shell structure consisting of an alloyed core of InAs(x)P(1-x), an intermediate shell of InP, and an outer shell of ZnSe were developed. The InAs(x)P(1-x) alloyed core has a graded internal composition with increasing arsenic content from the center to the edge of the dots. This compositional gradient results from two apparent effects: (1) the faster reaction kinetics of the phosphorus precursor compared to the arsenic precursor, and (2) a post-growth arsenic-phosphorus exchange reaction that increases the arsenic content. The cores have a zinc blend structure for all compositions and show tunable emission in the near-infrared (NIR) region. A first shell of InP leads to a red-shift and an increase in quantum yield. The final shell of ZnSe serves to stabilize the dots for applications in aqueous environments, including NIR biomedical fluorescence imaging. These NIR-emitting core/shell/shell InAs(x)P(1-x)/InP/ZnSe were successfully used in a sentinel lymph node mapping experiment.
Related Papers
- → Arsenic compounds in leaves and roots of radish grown in soil treated by arsenite, arsenate and dimethylarsinic acid(2002)65 cited
- → La2MgTiO6:Bi3+/Mn4+ photoluminescence materials: Molten salt preparation, Bi3+ → Mn4+ energy transfer and thermostability(2020)21 cited
- → Photoluminescence of porous Si, oxidized then deoxidized chemically(1992)109 cited
- → Study of delocalized and localized states in ZnSeO layers with photoluminescence, micro-photoluminescence, and time-resolved photoluminescence(2019)7 cited
- → Ballistic effect and new concept of Si wire photoluminescence(2003)1 cited