Phase Transition between Nanostructures of Titanate and Titanium Dioxides via Simple Wet-Chemical Reactions

Citations Over TimeTop 1% of 2005 papers

Abstract

Titanate nanofibers of various sizes and layered structure were prepared from inorganic titanium compounds by hydrothermal reactions. These fibers are different from "refractory" mineral substances because of their dimension, morphology, and significant large ratio of surface to volume, and, surprisingly, they are highly reactive. We found, for the first time, that phase transitions from the titanate nanostructures to TiO(2) polymorphs take place readily in simple wet-chemical processes at temperatures close to ambient temperature. In acidic aqueous dispersions, the fibers transform to anatase and rutile nanoparticles, respectively, but via different mechanisms. The titanate fibers prepared at lower hydrothermal temperatures transform to TiO(2) polymorphs at correspondingly lower temperatures because they are thinner, possess a larger surface area and more defects, and possess a less rigid crystal structure, resulting in lower stability. The transformations are reversible: in this case, the obtained TiO(2) nanocrystals reacted with concentrate NaOH solution, yielding hollow titanate nanotubes. Consequently, there are reversible transformation pathways for transitions between the titanates and the titanium dioxide polymorphs, via wet-chemical reactions at moderate temperatures. The significance of these findings arises because such transitions can be engineered to produce numerous delicate nanostructures under moderate conditions. To demonstrate the commercial application potential of these processes, we also report titanate and TiO(2) nanostructures synthesized directly from rutile minerals and industrial-grade rutiles by a new scheme of hydrometallurgical reactions.

Related Papers

• → The role of the surface intermediates in the photoelectrochemical behaviour of anatase and rutile TiO2(1993)240 cited
• → Photodegradation of organic dyes based on anatase and rutile TiO₂nanoparticles(2015)150 cited
• → Electrostatic potential calculations on crystalline TiO2: The surface reducibility of rutile and anatase(1983)33 cited
• → Infrared– active defects in a TiO2 mixture of coexisting anatase and rutile phases(2003)19 cited
• → 주형합성을 통한 메조포러스 TiO 2 제조 및 실리카 메조포어 내부에서의 TiO 2 상전이 거동 변화(2018)