Photocatalytic H2 Evolution Reaction from Aqueous Solutions over Band Structure-Controlled (AgIn)xZn2(1-x)S2 Solid Solution Photocatalysts with Visible-Light Response and Their Surface Nanostructures
Citations Over TimeTop 1% of 2004 papers
Abstract
(AgIn)(x)Zn(2(1-x))S(2) solid solutions between ZnS photocatalyst with a wide band gap and AgInS(2) with a narrow band gap showed photocatalytic activities for H(2) evolution from aqueous solutions containing sacrificial reagents, SO(3)(2)(-) and S(2)(-), under visible-light irradiation (lambda >or= 420 nm) even without Pt cocatalysts. Loading of the Pt cocatalysts improved the photocatalytic activity. Pt (3 wt %)-loaded (AgIn)(0.22)Zn(1.56)S(2) with a 2.3 eV band gap showed the highest activity for H(2) evolution, and the apparent quantum yield at 420 nm amounted to 20%. H(2) gas evolved at a rate of 3.3 L m(-2) x h(-1) under irradiation using a solar simulator (AM 1.5). The diffuse reflection and the photoluminescence spectra of the solid solutions shifted monotonically to a long wavelength side as the ratio of AgInS(2) to ZnS increased in the solid solutions. The photocatalytic H(2) evolution depended on the compositions as well as the photophysical properties. The dependence of the photophysical and photocatalytic properties upon the composition was mainly due to the change in the band position caused by the contribution of the Ag 4d and In 5s5p orbitals to the valence and conduction bands, respectively. It was found from SEM and TEM observations that the solid solutions partially had nanostep structures on their surfaces. The Pt cocatalysts were selectively photodeposited on the edge of the surface nanosteps. It was suggested that the specific surface nanostructure was effective for the suppression of recombination between photogenerated electrons and holes and for the separation of H(2) evolution sites from oxidation reaction sites.
Related Papers
- → AgInxGa1−xS2solid solution nanocrystals: synthesis, band gap tuning and photocatalytic activity(2014)22 cited
- → Solid solution InxGa1−x AsySbzP1−y−z : A new material for infrared optoelectronics. I. Thermodynamic analysis of the conditions for obtaining solid solutions, isoperiodic to InAs and GaSb substrates, by liquid-phase epitaxy(1997)13 cited
- → Synthesis and Basic Properties of Y1−xYbxVO4 Obtained by High-Energy Ball Milling and High-Temperature Treatment(2023)2 cited
- → CuCr2–xSbxS4 and Cu1–ySbyCr2S4 solid solutions(2000)5 cited
- Phase Relation and Formation Mechanism of the Ternary System Sn_(1-x-y)Mn_xSb_yO_2 Solid Solution(2011)